Pressure vessel steel plate and boiler steel plate P235GH and P265GH according to standard EN 10028_2 

are mainly specified in elevated temperature working surroundings.With the minimum yield strength at 

235 Mpa,P235GH shall be done Normalized heat treatment when rolling.P235GH steel plate are normally 

used to low strength welded boilers and pressure tanks&vessels.

P265GH pressure vessel plates are owned the minimum yield point at 265 Mpa strength which are normally 

used in higher strength situiations for boilers and tanks.P265GH steel also need to be done Normalized.

Other additional technical requirements for P265GH steel have to be drafted by our end user in their 

purchase orders.

 

Mechanical properties for P235GH pressure vessel steel plate:

Yield Strength (Min Mpa)			Tensile Strength ( Mpa)
t≤16	16<t≤40	40<t	t≤100	100<t≤150	150<t
235	225	215	360/480	350/480	340/480

 

Chemical composition of Ladle analysis for P235GH boiler steel plate (Max %):

C	Si	Mn	P	S	Al min	N	Cr
0.16	0.35	0.60/1.20	0.025	0.015	0.020	0.012	0.30
Cu	Mo	Nb	Ni	Ti	V	Cr+Cu+Mo+Ni
0.30	0.08	0.020	0.30	0.03	0.02	0.70