Pressure vessel and boiler steel plates P355ML1 and P355ML2 shall be done heat treatment under Thermomechanically rolled 

when rolling.This treatment offer good cold forming and hot forming properities without negatively affecting the material 

properties for steel plate P355ML1 and P355ML2. So these steel grades of P355ML1 and P355ML2 are therefore also suitable 

for cold_bordering and cold_flanging as well as for cold_bending and cold_folding.

 

As for the necessary technical terms for boiler steel sheet P355ML1,low temperature impacting test have to be done at minus 

40 ℃,however,for boiler steel sheet P355ML2,the temperature have to be at minus 50 ℃ at the single direction.Now YUSHENG 

STEEL also stock quantity of steel plates P355ML1 and P355ML2 for different thicknesses in our port warehouses.So please 

contact us now if you need a shortest delivery time for these plates.

 

Mechanical properties for P355ML1 pressure vessel steel plate:

Yield Strength (Min Mpa)			Tensile Strength  ( Mpa)
t≤16	16<t≤40	40<t
355	355	345	450/610

 

Chemical composition of cast analysis for P355ML1 boiler steel plate (Max %):

C	Si	Mn	P	S	Al total Min	N
0.14	0.50	1.60	0.020	0.015	0.020	0.015
Mo	Nb	Ni	Ti	V	Cr+Cu+Mo
0.20	0.05	0.50	0.05	0.10	0.60