Low alloy steel plate S355ML shall be rolling in TMCP also named thermomechanical rolled.For the steel 

igots of S355ML,our mill would make ingots by electric furnace,in this case,the purity of steel water 

would be approved hardly,so that the steel plate quality would be approved accordingly.

 

Our minimum rolling thickness for this steel grade S355ML shall be 8 milimeter,now there is no steel 

coils for S355ML in chinese current market owning to the technical limited in low temperature impacting 

test at minus 50 centi degree for these coils.Our maximum rolling thickness for steel plate S355ML 

can reach by 350mm.

 

Chemical composition of Ladle analysis for S355ML steel plate (Max %):

C	Si	Mn	P	S	Nb	V	Al total
0.14	0.50	1.60	0.025	0.020	0.05	0.10	≥0.02
Ti	Cr	Ni	Mo	Cu	N
0.05	0.30	0.50	0.10	0.55	0.015

 

Mechanical properties for S355ML steel plate:

Yield Strength (Min Mpa)				Tensile Strength ( Mpa)		Impacting Test
t≤16	16<t≤40	40<t≤100	100<t	t≤100	100<t	℃	J
355	345	335	320	470-630	430-590	-50	27