S550QL1 steel plate under EN10025_6 belongs to high yield strength structural steel.With the minimum yield 

strength at 550 Mpa for the thickness belows 50 millimeters,530 Mpa for the thickness between 50 and 100 

millimeters.S550QL1 have to do the low temperature impacting test at minus 60 centi degree with energy 27 J 

on transverse V_notch test pieces.

Yusheng iron and steel are supplying S550QL1 many years owning to the highest technical teams in Chinese 

steel mills.Our engineers have a guarantee for our steel property.Our steps contains technical requirements 

confirmation,checking rolling,and mill tests before delivery.Every step shall be careful and responsible.

 

Mechanical properties for S550QL1 steel plate:

Yield Strength (Min Mpa)			Tensile Strength ( Mpa)
t≤50	50<t≤100	100<t	t≤50	50<t≤100	100<t
550	530	490	640-820	640-820	590-770

 

Chemical composition of Ladle analysis for S550QL1 steel plate (Max %):

C	Si	Mn	P	S	N	B	Cr
0.20	0.80	1.70	0.020	0.010	0.015	0.005	1.50
Cu	Mo	Nb	Ni	Ti	V	Zr
0.50	0.70	0.06	2.0	0.05	0.12	0.15