Quenched and tempered heat treatment steel plate and sheet S690QL under EN 10025_6 standard is equal to the 

steel grade Q690E in Chinese GB standard. Both these two steels shall be done low temperature Charpy_V 

impacting test at minus 40 centi degree.At present,the maximum thickness for S690QL for our mill is till 200 

millimeter.If your needed thickness above 200mm,we have to submit this inquiry to our technical department for 

reviewing and make a trial rolling.

 

After rolling all the plates,the mill would issue original Mill Test Certificate for each plate which would draft all the test 

values about chemical composition,mechincal properity,impacting test,heat treatment and so on.Else,the Heat 

Number and Batch Number is necessary for tracking for the true steel plates.

 

Chemical composition of Ladle analysis for S690QL steel plate (Max %):

C	Si	Mn	P	S	N	B	Cr
0.20	0.80	1.70	0.020	0.010	0.015	0.005	1.50
Cu	Mo	Nb	Ni	Ti	V	Zr
0.50	0.70	0.06	2.0	0.05	0.12	0.15

 

Mechanical properties for S690QL steel plate:

Yield Strength (Min Mpa)			Tensile Strength ( Mpa)
t≤50	50<t≤100	100<t	t≤50	50<t≤100	100<t
690	650	630	770-940	760-930	710-900